Hot Sale ASME Uns N10665 Hastelloy C276 C22 B3 B2 Wire for Industry

• Customization: Available
• Application: Aviation, Electronics, Industrial, Medical, Chemical
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Model NO.: Hastelloy C276 C22 B3 B2
• Purity: Nickel-Based
• Alloy: Alloy
• Type: Nickel Wire
• Powder: Not Powder
• Surface: Bright, Oxidized Color, Acid White
• Density: 8.19 G/Cm
• Melting Point: 1260-1340 C
• Ultimate Strength: 462MPa
• Transport Package: Spool
• Specification: 0.1~10mm
• Trademark: DLX
• Origin: Jiangsu
• HS Code: 7505220000
• Production Capacity: 999999999

Product Description

High quality Nickel Alloy ASTM B335 Hastelloy B2 Wire manufacturer

Hastelloy B2 is a solid solution strengthened, nickel-molybdenum alloy, with significant resistance to reducing environments like hydrogen chloride gas, and sulfuric, acetic and phosphoric acids. Molybdenum is the primary alloying element which provides significant corrosion resistance to reducing environments. This nickel steel alloy can be used in the as-welded condition because it resists the formation of grain-boundary carbide precipitates in the weld heat-affected zone.

This nickel alloy provides excellent resistance to hydrochloric acid at all concentrations and temperatures. In additions, Hastelloy B2 has excellent resistance to pitting, stress corrosion cracking and to knife-line and heat-affected zone attack. Alloy B2 provides resistance to pure sulfuric acid and a number of non-oxidizing acids.

Alloy B-2 has poor corrosion resistance to oxidizingenvironments, therefore, it is not recommended for use in oxidizing media or in the presence of ferric or cupric salts because they may cause rapid premature corrosion failure. These salts may develop when hydrochloric acid comes in contact with iron and copper. Therefore, if this alloy is used in conjunction with iron or copper piping in a system containing hydrochloric acid, the presence of these salts could cause the alloy to fail prematurely. In addition, this nickel steel alloy should not be used at temperatures between 1000° F and 1600° F because of a reduction in the ductility in the alloy.

Process	Diameter	Voltage	Amperage	Gas
TIG	.045"     (1.2mm)	13-16	80-110	100% Argon
	1/16"     (1.6mm)	14-18	90-130	100% Argon
	3/32"     (2.4mm)	15-20	120-175	100% Argon
	1/8"      (3.2mm)	15-20	150-220	100% Argon
MIG	.045"     (1.2mm)	28-32	180-220	75% Argon + 25% Helium
	1/16"     (1.6mm)	29-33	200-250	75% Argon + 25% Helium
SAW	3/32"     (2.4mm)	28-30	275-350	Suitable Flux may be used
	1/8"      (3.2mm)	29-32	350-450	Suitable Flux may be used
	5/32"     (4.0mm)	30-33	400-550	Suitable Flux may be used

Hastelloy	Density g/cm3	Melting point ºC	Elongation A5 %	Tensile Strength Rm N/mm2	Yield Strength RP0.2N/mm2
C-276	8.9	1325-1370ºC	62	758	363
C-22	8.9	1325-1370 ºC	40	690	283
C-2000	8.5	1399ºC 2550°F	45	690	283
B-2	9.2	1330-1380ºC	40	745	325
B-3	9.22	1370-1418ºC	40	760	350
G-30	8.22	1399ºC 2550°F	62	524	200
X	8.3	1260-1355ºC	30	690	/
C-4	8.64	399°C 2550°F	40	690	280
G-35	8.22	1370-1400ºC	/	/	/
C	8.94	1330-1380 ºC	40	690	310

 

 

 

 

FAQ

Question: Are you a trading company or manufacturer?
Answer: We're manufacturer.

Question2:  Could you help to design the product?

Answer:  Yes, we have excellent R&D team, OEM/ODM orders are all welcome.

 

Question: Could you supply samples?

Answer: Yes, wecould supply samples according to your requirement.

Question: could we visit your factory?
Answer: Sure, factory visit is warmly welcome.